Studies were conducted to determine the friction and wear properties of experimental carbon-graphites. Hemispherically tipped carbon-graphite rider specimens were tested in sliding contact with rotating Inconel X-750 disks in air. A surface speed of 1.33 m/sec, a load of 500 g, and a specimen temperature of 650 C were used. Results indicate: (1) hardness is not a major factor in determining friction and wear under the conditions of these studies. (2) Friction and wear as low as or lower than those observed for a good commercial seal material were attained with some of the experimental materials studied. (3) The inclusion of boron carbide (as an oxidation inhibitor) has a strong influence on wear rate. (4) Phosphate treatment reduces the friction coefficient when boron carbide is not present in the base material.